300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel. Some ...
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an alloy of iron that is resistant to rusting and corrosion. It contains iron with chromium and other elements such as molybdenum , carbon , nickel and nitrogen depending on its specific use and cost.
Type 310 310S— is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the steel excellent oxidation resistance as well as high strength at high temperature. This grade is also very ductile, and has good weldability enabling its widespread usage in many applications. [7]
Pitting resistance equivalent number (PREN) is a predictive measurement of a stainless steel's resistance to localized pitting corrosion based on its chemical composition. In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride .
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
The pitting corrosion resistance of stainless steels is estimated by the pitting resistance equivalent number (PREN). PREN = %Cr + 3.3%Mo + 16%N Where the Cr, Mo, and N, terms correspond to the contents by weight % of chromium , molybdenum and nitrogen respectively in the steel.
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.