Ti-6Al-4V titanium alloy commonly exists in alpha, with hcp crystal structure, (SG : P63/mmc) and beta, with bcc crystal structure, (SG : Im-3m) phases. While mechanical properties are a function of the heat treatment condition of the alloy and can vary based upon properties, typical property ranges for well-processed Ti-6Al-4V are shown below.
Grade 5 also known as Ti6Al4V, Ti-6Al-4V or Ti 6-4 Turbine blade made from Ti alloy not to be confused with Ti-6Al-4V-ELI (Grade 23), is the most commonly used alloy. It has a chemical composition of 6% aluminum, 4% vanadium, 0.25% (maximum) iron, 0.2% (maximum) oxygen, and the remainder titanium. [19]
Ti-6Al-2Sn-4Zr-2Mo (UNS designation R54620), also known as Ti 6-2-4-2, is a near alpha titanium alloy known for its high strength and excellent corrosion resistance. It is often used in the aerospace industry for creating high-temperature jet engines and the automotive industry to create high performance automotive valves.
Naturally occurring titanium is composed of five stable isotopes: 46 Ti, 47 Ti, 48 Ti, 49 Ti, and 50 Ti, with 48 Ti being the most abundant (73.8% natural abundance). At least 21 radioisotopes have been characterized, the most stable of which are 44 Ti with a half-life of 63 years; 45 Ti, 184.8 minutes; 51 Ti, 5.76 minutes; and 52 Ti, 1.7 minutes.
This was the first large-scale use of this material on a commercial jet engine [4] when it entered service in 2011. [5] The TiAl LPT blades are cast by Precision Castparts Corp. and Avio s.p.a. Machining of the Stage 6, and Stage 7 LPT blades is performed by Moeller Manufacturing.
Ti-6Al-7Nb (UNS designation R56700) is an alpha-beta titanium alloy first synthesized in 1977 containing 6% aluminum and 7% niobium. It features high strength and has similar properties as the cytotoxic vanadium containing alloy Ti-6Al-4V. Ti-6Al-7Nb is used as a material for hip prostheses. [1]
The zirconium and titanium based Liquidmetal alloys achieved yield strength of over 1723 MPa, nearly twice the strength of conventional crystalline titanium alloys (Ti 6 Al 4 V is ~830 MPa), and about the strength of high-strength steels and some highly engineered bulk composite materials (see tensile strength for a list of common materials ...