Young's modulus is the slope of the linear part of the stress–strain curve for a material under tension or compression.. Young's modulus (or Young modulus) is a mechanical property of solid materials that measures the tensile or compressive stiffness when the force is applied lengthwise.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The tensile strength can be quoted as either true stress or engineering stress, but engineering stress is the most commonly used. Fatigue strength is a more complex measure of the strength of a material that considers several loading episodes in the service period of an object, [ 6 ] and is usually more difficult to assess than the static ...
In engineering and materials science, a stress–strain curve for a material gives the relationship between stress and strain. It is obtained by gradually applying load to a test coupon and measuring the deformation , from which the stress and strain can be determined (see tensile testing ).
Approximate specific stiffness for various materials. No attempt is made to correct for materials whose stiffness varies with their density. Material Young's modulus Density (g/cm 3) Young's modulus per density; specific stiffness (10 6 m 2 s −2) Young's modulus per density squared (10 3 m 5 kg −1 s −2) Young's modulus per density cubed ...
In materials science, a general rule of mixtures is a weighted mean used to predict various properties of a composite material. [1] [2] [3] It provides a theoretical upper- and lower-bound on properties such as the elastic modulus, ultimate tensile strength, thermal conductivity, and electrical conductivity. [3]
Young's modulus (E) - apply small, incremental changes in the lattice parameter along a specific axis and compute the corresponding stress response using DFT. Young’s modulus is then calculated as E=σ/ϵ, where σ is the stress and ϵ is the strain. [4] Initial structure: Start with a relaxed structure of the material.
The relation between stress and its effects and causes, including deformation and rate of change of deformation, can be quite complicated (although a linear approximation may be adequate in practice if the quantities are small enough). Stress that exceeds certain strength limits of the material will result in permanent deformation (such as ...