Castability is the ease of forming a quality casting. [1] A very castable part design is easily developed, incurs minimal tooling costs, requires minimal energy, and has few rejections. [2] Castability can refer to a part design or a material property. [1]
Directional solidification is the preferred technique for casting high temperature nickel-based superalloys that are used in turbine engines of aircraft. Some microstructural problems such as coarse dendritic structure, long dendrite side branches, and porosity hinder the full potential of single crystal ni-based alloys. [ 6 ]
Cast iron casting. Casting is a manufacturing process in which a liquid material is usually poured into a mold, which contains a hollow cavity of the desired shape, and then allowed to solidify. The solidified part is also known as a casting, which is ejected or broken out of the mold to complete the process.
A core is a device used in casting and moulding processes to produce internal cavities and reentrant angles (an interior angle that is greater than 180°). The core is normally a disposable item that is destroyed to get it out of the piece. [1] They are most commonly used in sand casting, but are also used in die casting and injection moulding.
The exact process and pattern equipment is always determined by the order quantities and the casting design. Sand casting can produce as little as one part, or as many as a million copies. Although additive manufacturing modalities such as SLS or SLM have potential to replace casting for some production situations, casting is still far from ...
A chill is an object used to promote solidification in a specific portion of a metal casting mold. Normally the metal in the mould cools at a certain rate relative to thickness of the casting. When the geometry of the molding cavity prevents directional solidification from occurring naturally, a chill can be strategically placed to help promote it.
Draft angle design is an important factor when designing plastic parts. Because of shrinkage of plastic material, injection molded parts have a tendency to shrink onto a core. This creates higher contact pressure on the core surface and increases friction between the core and the part, thus making ejection of the part from the mold difficult.
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots .