v. t. e. Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [1][2]
Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture. Rust consists of hydrous iron (III) oxides (Fe 2 O 3 ·nH 2 O) and iron (III) oxide-hydroxide (FeO (OH), Fe (OH) 3), and is typically associated with the corrosion of refined iron.
Galvanic corrosion. Corrosion of an iron nail wrapped in bright copper wire, showing cathodic protection of copper; a ferroxyl indicator solution shows colored chemical indications of two types of ions diffusing through a moist agar medium. Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an electrochemical ...
Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal. The driving power for pitting corrosion is the depassivation of a small area, which becomes anodic (oxidation reaction) while an unknown but potentially vast area becomes cathodic (reduction reaction), leading to ...
Corrosion engineering is an engineering specialty that applies scientific, technical, engineering skills, and knowledge of natural laws and physical resources to design and implement materials, structures, devices, systems, and procedures to manage corrosion. [1] From a holistic perspective, corrosion is the phenomenon of metals returning to ...
Stress corrosion cracking (SCC) is the growth of crack formation in a corrosive environment. It can lead to unexpected and sudden failure of normally ductile metal alloys subjected to a tensile stress, especially at elevated temperature. SCC is highly chemically specific in that certain alloys are likely to undergo SCC only when exposed to a ...
Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet conditions. Chemical damage is caused by the formation of expansive products produced by chemical reactions (from carbonatation, chlorides, sulfates ...
Microbial corrosion, also known as microbiologically influenced corrosion (MIC), microbially induced corrosion (MIC) or biocorrosion, occurs when microbes affect the electrochemical environment of the surface on which they are fixed. This usually involves the formation of a biofilm, which can either increase the corrosion of the surface or, in ...