4301-304-00-I and X5CrNi18-9, the ISO 15510 name and designation. UNS S30400 in the unified numbering system. A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent ...
Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel). [6] The Japanese equivalent grade of this material is SUS304.
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
The grade 304 stainless steel family of SAE steel grades Topics referred to by the same term This disambiguation page lists articles associated with the same title formed as a letter–number combination.
Martensitic stainless steels can be high- or low-carbon steels built around the composition of iron, 12% up to 17% chromium, carbon from 0.10% (Type 410) up to 1.2% (Type 440C): [8] The chromium and carbon contents are balanced to have a martensitic structure.
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
UNS K11547 is T2 tool steel; UNS S17400 is ASTM grade 630, Cr-Ni 17-4PH precipitation hardened stainless steel; UNS S30400 is SAE 304, Cr/Ni 18/10, Euronorm 1.4301 stainless steel; UNS S31600 is SAE 316; UNS S31603 is 316L, a low carbon version of 316. The digits "03" were assigned since the maximum allowed carbon content is 0.03%; UNS C90300 ...