Chemical coloring of metals is the process of changing the color of metal surfaces with different chemical solutions. The chemical coloring of metals can be split into three types: electroplating – coating the metal surface with another metal using electrolysis. patination – chemically reacting the metal surface to form a colored oxide or ...
The pulse electroplating or pulse electrodeposition (PED) process involves the swift alternating of the electrical potential or current between two different values, resulting in a series of pulses of equal amplitude, duration, and polarity, separated by zero current. By changing the pulse amplitude and width, it is possible to change the ...
Such zinc electroplating or zinc alloy electroplating maintains a dominant position among other electroplating process options, based upon electroplated tonnage per annum. According to the International Zinc Association, more than 5 million tons are used yearly for both hot-dip galvanization and electroplating. [ 1 ]
Transition metal compounds are often colored because of transitions of electrons between d-orbitals of different energy. (see Transition metal#Colored compounds ). Organic compounds tend to be colored when there is extensive conjugation , causing the energy gap between the HOMO and LUMO to decrease, bringing the absorption band from the UV to ...
Electrochemical coloring of metals is a process in which the surface color of metal is changed by electrochemical techniques, i.e. cathodic or anodic polarization. The first method of electrochemical coloring of metals are certainly Nobili's colored rings, discovered by Leopoldo Nobili , an Italian physicist in 1826.
Copper electroplating takes place in an electrolytic cell using electrolysis. As with all plating processes, the part to be plated must be cleaned before depositing metal to remove soils, grease, oxides, and defects. [4] [5] After precleaning, the part is immersed in the cell's aqueous electrolyte solution and functions as the cathode.
The metal is deposited on the cathode. In a practical sense, this idealized process is complicated by some or all of the following considerations: the metal content is low (a few percent is typical), other metals deposit competitively with the desired one, the ore is not easily or efficiently dissolved.
Certain metals, such as zinc, may become embrittled from the hydrogen gas which is evolved at the cathode. The anodic process avoids this effect since oxygen is being generated at the anode. The major advantages that are normally touted for the cathodic processes are: Higher levels of corrosion protection are possible.