7085 aluminum alloy is wrought type alloy. ... Chemical composition. Properties [1] Value Density 2.85 g/cc Elements [1] Weight Percentage (%)
Welded aluminium alloy bicycle frame, made in the 1990s. An aluminium alloy (UK/IUPAC) or aluminum alloy (NA; see spelling differences) is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper, magnesium, manganese, silicon, tin, nickel and zinc.
1 Chemical composition. 2 Properties. 3 Aluminium alloy table. 4 References. Toggle the table of contents. ... Value Aluminum 91.9 - 95.4% Chromium ≤ 0.10%
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005 , 6061 , and 6063 ), although it is not strongly featured in ASTM (North American) standards.
7000 series alloys such as 7075 are often used in transport applications due to their high specific strength, including marine, automotive and aviation. [ 7 ] [ 14 ] These same properties lead to its use in rock climbing equipment, bicycle components, inline-skating-frames and hang glider airframes are commonly made from 7075 aluminium alloy.
1100 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). With a minimum of 99.0% aluminium, it is the most heavily alloyed of the 1000 series. It is also the mechanically strongest alloy in the series, and is the only 1000-series alloy commonly used in rivets.
6005 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is closely related, but not identical, to 6005A aluminium alloy. The main difference between the two alloys is that 6005 has a higher minimum composition percentage of aluminium than 6005A (while having essentially the same maximum).
1 Chemical Composition. ... 1200 Aluminium alloy has aluminium as the major element, ... Value Young's modulus: 69 GPa Elongation at break: 5.1%