The role of the cold end of glass container production is to complete the final tasks in the manufacturing process: spray on a polyethylene coating for abrasion resistance and increased lubricity, inspect the containers for defects, label the containers, and package the containers for shipment.
The Fourcault process is a method of manufacturing plate glass. First developed in Belgium by Émile Fourcault (1862–1919) during the early 1900s, the process was used globally. Fourcault is an example of a "vertical draw" process, in that the glass is drawn against gravity in an upward direction. [1] Gravity forces influence parts of the ...
The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, [4] which pioneered the technique in the 1950s at their production site in St Helens, Merseyside. [5] Modern windows are usually made from float glass, [6] though Corning Incorporated uses the overflow downdraw method. [7]
This process is only suitable for high production volumes. For smaller production volumes, the preforms have to be manufactured by mechanical material-removing steps from blocks or slices of raw glass. Precision glass moulding: In this step the preform is directly formed into an optical glass lens.
Until the 20th century, window glass production involved blowing a cylinder and flattening it. [9] Two major methods to make window glass, the crown method and the cylinder method, were used until the process was changed much later in the 1920s. [10] All glass products must then be cooled gradually , or else they could easily break. [11]
Glass (1958 film) Glass bead making; Glass casting; Glass cone; Glass cutter; Glass fiber; Glass melting furnace; Glass production in Licking County, Ohio; Glass recycling; Glassblowing; Glassmakers' symbol; Glassmaking at Blenko Glass Company
The manufacturing process for soda–lime glass consists in melting the raw materials, which are the silica, soda (Na 2 O), hydrated lime (Ca(OH) 2), dolomite (CaMg(CO 3) 2, which provides the magnesium oxide), and aluminium oxide; along with small quantities of fining agents (e.g., sodium sulfate (Na 2 SO 4), sodium chloride (NaCl), etc.) in a glass furnace at temperatures locally up to 1675 ...
In manufacturing, glass-ceramics are valued for having the strength of ceramic but the hermetic sealing properties of glass. Glass-ceramics are mostly produced in two steps: First, a glass is formed by a glass-manufacturing process, after which the glass is cooled down. Second, the glass is put through a controlled heat treatment schedule.