In SI units, permeability is measured in henries per meter (H/m), or equivalently in newtons per ampere squared (N/A 2). The permeability constant μ 0, also known as the magnetic constant or the permeability of free space, is the proportionality between magnetic induction and magnetizing force when forming a magnetic field in a classical vacuum.
Ferromagnetism is a property of certain materials (such as iron) that results in a significant, observable magnetic permeability, and in many cases, a significant magnetic coercivity, allowing the material to form a permanent magnet. Ferromagnetic materials are noticeably attracted to a magnet, which is a consequence of their substantial ...
To describe a soft ferromagnetic material for technical use, the following parameters are specified: (Relative) permeability Ratio of induction B in the material caused by some field H to an induction in a vacuum in the same field; it is a dimensionless value, as it is relative to a vacuum permeability;
"Soft" magnetic materials with low coercivity and hysteresis, such as silicon steel, or ferrite, are usually used in cores. Magnetic field (green) created by a current-carrying winding (red) in a typical magnetic core transformer or inductor, with the iron core C forming a closed loop, possibly with air gaps G in it. The drawing shows a section ...
Different materials have different saturation levels. For example, high permeability iron alloys used in transformers reach magnetic saturation at 1.6–2.2 teslas (T), [4] whereas ferrites saturate at 0.2–0.5 T. [5] Some amorphous alloys saturate at 1.2–1.3 T. [6] Mu-metal saturates at around 0.8 T. [7] [8]
For example, the CGS volume magnetic susceptibility of water at 20 °C is 7.19 × 10 −7, which is 9.04 × 10 −6 using the SI convention, both quantities being dimensionless. Whereas for most electromagnetic quantities, which system of quantities it belongs to can be disambiguated by incompatibility of their units, this is not true for the ...
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
The coercivity is a measure of the degree of magnetic hysteresis and therefore characterizes the lossiness of soft magnetic materials for their common applications. The saturation remanence and coercivity are figures of merit for hard magnets, although maximum energy product is also commonly quoted.