Normalizing not only produces pearlite but also martensite and sometimes bainite, which gives harder and stronger steel but with less ductility for the same composition than full annealing. In the normalizing process the steel is heated to about 40 degrees Celsius above its upper critical temperature limit, held at this temperature for some ...
Tempering is a process of heat treating, which is used to increase the toughness of iron-based alloys. Tempering is usually performed after hardening, to reduce some of the excess hardness, and is done by heating the metal to some temperature below the critical point for a certain period of time, then allowing it to cool in still air. The exact ...
The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F), depending on the alloy in question. This process is mainly suited for low-carbon steel. The material is heated up to a temperature just below the lower critical temperature of steel.
As with conventional quench and tempering the material being heat treated must be cooled from the austenitizing temperature quickly enough to avoid the formation of pearlite. The specific cooling rate that is necessary to avoid the formation of pearlite is a product of the chemistry of the austenite phase and thus the alloy being processed.
Equipment. Consolidated Engineering Company Archived 2013-11-05 at the Wayback Machine Annealing furnaces cover a broad range of Steel and Aluminum applications including tempering, normalizing, and aging, and similar automated loading, unloading and natural or forced cooling is possible with roller hearth, tip-up or batch arrangements.
The recrystallization temperature is temperature at which recrystallization can occur for a given material and processing conditions. This is not a set temperature and is dependent upon factors including the following: [3] Increasing annealing time decreases recrystallization temperature
A metallurgic process used in annealing; Normalization (image processing), changing the range of pixel intensity values; Audio normalization, a process of uniformly increasing or decreasing the amplitude of an audio signal; Data normalization, general reduction of data to canonical form
Gas carburizing is normally carried out at a temperature within the range of 900 to 950 °C. In oxy-acetylene welding, a carburizing flame is one with little oxygen, which produces a sooty, lower-temperature flame. It is often used to anneal metal, making it more malleable and flexible during the welding process.