ASTM A572 steel is a common high strength, ... A572 steel has five different grades: 42, 50, 55, 60 and 65. [2] ... A572 Grade Yield Point (KSI) [MPa] ...
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [ 2 ]
In US use, the grade designation is equal to the minimum yield strength of the bar in ksi (1000 psi); for example, grade 60 rebar has a minimum yield strength of 60 ksi. Rebar is most commonly manufactured in grades 40, 60, and 75 with higher strength readily available in grades 80, 100, 120 and 150.
The SAE steel grades ... a 1060 steel is a plain-carbon steel containing 0.60 ... but also nitrogen is added to obtain a much higher yield and tensile strength than ...
A common type of micro-alloyed steel is improved-formability HSLA. It has a yield strength up to 80,000 psi (550 MPa) but costs only 24% more than A36 steel (36,000 psi (250 MPa)). One of the disadvantages of this steel is that it is 30 to 40% less ductile.
Yield strength (MPa) Ultimate strength (MPa) ASTM A36 steel: 250: 400 Steel, API 5L X65 [2] 448: 531 Steel, high strength alloy ASTM A514: 690: 760 Steel, prestressing strands 1650: 1860 Piano wire 1740–3300 [3] Carbon fiber (CF, CFK) 5650 [4] High-density polyethylene (HDPE) 26–33: 37 Polypropylene: 12–43: 19.7–80 Stainless steel AISI ...
ASTM A992 is currently the most available steel type for structural wide-flange beams. The industry's technical institute describes the standard thus: "ASTM A992 (Fy = 50 ksi, Fu = 65 ksi) is the preferred material specification for wide-flange shapes, having replaced ASTM A36 and A572 grade 50. There are a couple of noteworthy enhancements ...
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).