6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
Elastic properties describe the reversible deformation (elastic response) of a material to an applied stress.They are a subset of the material properties that provide a quantitative description of the characteristics of a material, like its strength.
The shear modulus is one of several quantities for measuring the stiffness of materials. All of them arise in the generalized Hooke's law: . Young's modulus E describes the material's strain response to uniaxial stress in the direction of this stress (like pulling on the ends of a wire or putting a weight on top of a column, with the wire getting longer and the column losing height),
4 Aluminium alloy table. ... 2017 Aluminium alloy has copper, iron, ... Elastic modulus: 72 GPa Shear strength (annealed) 124 MPa Thermal properties
By comparison, annealed type 316 stainless steel has a density of 8000 kg/m 3, modulus of 193 GPa, and tensile strength of 570 MPa. [23] Tempered 6061 aluminium alloy has a density of 2700 kg/m 3, modulus of 69 GPa, and tensile strength of 310 MPa, respectively. [24] Ti-6Al-4V standard specifications include: [25] [26]
Aluminum 1100–O (annealed) 0.20: 180 2024 aluminum alloy (heat treated—T3) 0.16: 690 5052-O 0.13 210 Aluminum 6061–O (annealed) 0.20: 205 Aluminum 6061–T6: 0.05: 410 Aluminum 7075–O (annealed) 0.17: 400 Brass, Naval (annealed) 0.49: 895 Brass 70–30 (annealed) 0.49: 900 Brass 85–15 (cold-rolled) 0.34: 580 Cobalt-base alloy (heat ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Alloys with higher copper content (alloyings 6061, 6056, 6013) are mainly used in aviation. Iron occurs in all aluminium alloys as an impurity in quantities of 0.05-0.5%. It forms the phases Al8Fe2Si, Al5FeSi and Al8FeMg3Si6, which are all thermally stable, but undesirable because they brittle the material. Silicon surpluses are also used to ...