Degraded concrete and rusted, exposed reinforcement bar (rebar) on Welland River bridge of the Queen Elizabeth Way in Niagara Falls, Ontario. Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet ...
Download as PDF; Printable version; In other projects Wikidata item; ... Pages in category "Concrete degradation" The following 3 pages are in this category, out of 3 ...
A fairly well-defined reaction front can often be observed in thin sections; ahead of the front the concrete is normal, or near normal. Behind the reaction front, the composition and the microstructure of concrete are modified. These changes may vary in type or severity but commonly include: Extensive cracking; Expansion
Calcium aluminates can form complex salts in combination with different types of anions.Two series of calcium aluminates are known in cement chemistry: AFm and AFt phases, being respectively mono- or tri-substituted with a given divalent anion X (e.g. SO 2− 4, CO 2− 3, or hosting a divalent impurity such as SeO 2− 4 [3]...), or with two units of a monovalent anion, e.g. OH −, Cl − ...
The presence of chlorides to the steel surface, above a certain critical amount, can locally break the protective thin film of oxides on the steel surface, even if concrete is still alkaline, causing a very localized and aggressive form of corrosion known as pitting. Current regulations forbid the use of chloride contaminated raw materials ...
C 131–03. Standard Test Method for Resistance to Degradation of Small-Size Coarse Aggregate by Abrasion and Impact in the Los Angeles Machine. ASTM International. Lavin, P. (2003). Asphalt Pavements: A Practical Guide to Design, Production and Maintenance for Engineers and Architects. CRC Press. ISBN 978-0-203-45329-2. Woolf, D.; Runner, D ...
ASTM C1293: "Test Method for Concrete Aggregates by Determination of Length Change of Concrete Due to Alkali-Silica Reaction". It is a long-term confirmation test (1 or 2 years) at 38 °C in a water-saturated moist atmosphere (inside a thermostated oven) with concrete prisms containing the aggregates to be characterised mixed with a high-alkali ...
Sulfate attacks, an hat appellation covering different concrete degradation mechanisms: Delayed ettringite formation (DEF), also known as internal sulfate attack (ISA) when the temperature of fresh concrete exceeds 65 °C during its setting and hardening; External sulfate attack (ESA), and; Thaumasite form of sulfate attack (TSA).