It is filled with a sample of the plating solution and an appropriate anode which is connected to a rectifier. The "work" is replaced with a Hull cell test panel that will be plated to show the "health" of the bath. The Hull cell is a trapezoidal container that holds 267 milliliters of a plating bath solution.
A sulfate-based bath that uses insoluble catalytic anodes, which maintains an electrode potential that prevents oxidation. The trivalent chromium-plating process can plate the workpieces at a similar temperature, rate and hardness, as compared to hexavalent chromium. Plating thickness ranges from 5 to 50 μin (0.13 to 1.27 μm). [2]
The cathode efficiency depends on the process and varies between 90 and 97%. Due to this mismatch, during the plating the nickel concentration in the solution and the pH will slowly rise. [6] The process takes minutes to hours depending on the current density and the intended thickness of the plating. [7]
The main ingredients of an electroless nickel plating bath are source of nickel cations Ni 2+, usually nickel sulfate and a suitable reducing agent, such as hypophosphite H 2 PO − 2 or borohydride BH − 4. [1] With hypophosphite, the main reaction that produces the nickel plating yields orthophosphite H 2 PO − 3, elemental phosphorus ...
High zinc improves the bath's efficiency (plating speed), while lower levels improve the bath's ability to throw into low current densities. Typically, the Zn metal level varies between 20 and 50 g/L (2.7-6.7 oz/gal). The pH varies between 4.8 and 5.8 units. The following chart illustrates a typical all potassium chloride bath composition:
The formula was meant to be dissolved in water at the concentration of 9.0 g/L, giving a bath with pH = 1.5. It yielded a light gold color after 1 min, and a golden-brown film after 3 min. The average thickness ranged between 200 and 1000 nm. [6] Iridite 14-2 is a chromate conversion bath for aluminum.
Copper plating on aluminium. Copper electroplating is the process of electroplating a layer of copper onto the surface of a metal object. Copper is used both as a standalone coating and as an undercoat onto which other metals are subsequently plated. [1]
Gold plating is a method of depositing a thin layer of ... The thickness of gold plating on jewellery is noted in microns (or micro-meters). ... An acid bath is ...