Process annealing, also called intermediate annealing, subcritical annealing, or in-process annealing, is a heat treatment cycle that restores some of the ductility to a product being cold-worked so it can be cold-worked further without breaking. The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F ...
Time-Temperature-Transformation diagram for two steels: one with 0.4% wt. C (red line) and one with 0.4% wt. C and 2% weight Mn (green line). P = pearlite, B = bainite and M = martensite. Isothermal transformation diagrams (also known as time-temperature-transformation ( TTT ) diagrams ) are plots of temperature versus time (usually on a ...
The International Annealed Copper Standard (IACS) is a standard established in 1914 by the United States Department of Commerce. [1] It is an empirically derived standard value for the electrical conductivity of commercially available copper. Sometime around 1913 several copper samples from 14 important refiners and wire manufacturers were ...
Critical temperature. Following from the previous rule it is found that recrystallization requires a minimum temperature for the necessary atomic mechanisms to occur. This recrystallization temperature decreases with annealing time. Critical deformation. The prior deformation applied to the material must be adequate to provide nuclei and ...
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel. In superalloys, it is known to cause yield ...
Tempering (metallurgy) Differentially tempered steel. The various colors produced indicate the temperature the steel was heated to. Light straw indicates 204 °C (399 °F) and light blue indicates 337 °C (639 °F). [1][2] Tempering is a process of heat treating, which is used to increase the toughness of iron -based alloys.
Hollomon–Jaffe parameter. The Hollomon–Jaffe parameter (HP), also generally known as the Larson–Miller parameter, [1] describes the effect of a heat treatment at a temperature for a certain time. [2] This parameter is especially used to describe the tempering of steels, so that it is also called tempering parameter.
The Kirkendall effect is the motion of the interface between two metals that occurs due to the difference in diffusion rates of the metal atoms. The effect can be observed for example by placing insoluble markers at the interface between a pure metal and an alloy containing that metal, and heating to a temperature where atomic diffusion is reasonable for the given timescale; the boundary will ...