The goal of any synthetic method for nanomaterials is to yield a material that exhibits properties that are a result of their characteristic length scale being in the nanometer range (1 – 100 nm). Accordingly, the synthetic method should exhibit control of size in this range so that one property or another can be attained.
One of the more important applications of sol–gel processing is to carry out zeolite synthesis. Other elements (metals, metal oxides) can be easily incorporated into the final product and the silicate sol formed by this method is very stable. Semi-stable metal complexes can be used to produce sub-2 nm oxide particles without thermal treatment.
The template method to be described in the following has the advantage such that it allows the preparation of nanotubes and nanorods with very high precision. The method is based on the use of well defined porous templates, such as porous aluminum or silicon. The basic concept of this method is to exploit wetting processes. A polymer melt or ...
The top-down approach is breaking down of a system into small components, while bottom-up is assembling sub-systems into larger system. [15] A bottom-up approach for nano-assembly is a primary research target for nano-fabrication because top down synthesis is expensive (requiring external work) and is not selective on very small length scales, but is currently the primary mode of industrial ...
The synthesis of nanocomposite hydrogels is a process that requires specific material and method. These polymers need to be made up of equally spaced out, 30 nm in diameter, clay platelets that can swell and exfoliate in the presence of water.
CBD synthesis of these films allows for both cost-effective and accurate assemblies, with grain type and size as well as optical properties of the nanomaterial dictated by the properties of the surrounding bath. As such, this method of nanoscale chemosynthesis is often implemented when these properties are desired, and can be used for a wide ...
This method allows precise control over shape and size (monodisperse), but at the cost of long synthesis times and the inability to observe growth in real-time. More specialized techniques include sol-gel processing (hydrolysis and polycondensation of metal alkoxides), and combustion (flame) synthesis, which are rapid, non-solution phase pathways.
The synthesis efficiency is about 100 times higher than for the laser ablation method. The time required to make SWNT forests of the height of 2.5 mm by this method was 10 minutes in 2004. Those SWNT forests can be easily separated from the catalyst, yielding clean SWNT material (purity >99.98%) without further purification.