5052 is an aluminium–magnesium alloy, primarily alloyed with magnesium and chromium. 5052 is not a heat treatable aluminum alloy, but can be hardened through cold working. [ 2 ] Chemical properties
Aluminium is widely used in sheet metal form due to its flexibility, wide range of options, cost effectiveness, and other properties. [6] The four most common aluminium grades available as sheet metal are 1100-H14, 3003-H14, 5052-H32, and 6061-T6. [5] [7] Grade 1100-H14 is commercially pure aluminium, highly chemical and weather resistant.
Aluminium alloys are alloys where the principal metal is aluminium ... 4043 aluminium alloy; 5005 aluminium alloy; 5052 aluminium alloy; 5059 aluminium alloy;
The TSI Rolling Stock (2002/735/EC) has taken over the UIC Gauges definitions defining Kinematic Gauges with a reference profile such that Gauges GA and GB have a height of 4.35 m (14 ft 3 in) (they differ in shape) with Gauge GC rising to 4.70 m (15 ft 5 in) allowing for a width of 3.08 m (10 ft 1 in) of the flat roof. [7]
Note that the term aircraft aluminium or aerospace aluminium usually refers to 7075. [65] [66] 4047 aluminium is a unique alloy used in both the aerospace and automotive applications as a cladding alloy or filler material. As filler, aluminium alloy 4047 strips can be combined to intricate applications to bond two metals. [67]
The use of larger gauge stranded aluminum wire (larger than #8 AWG) is fairly common in much of North America for modern residential construction. Aluminum wire is used in residential applications for lower voltage service feeders from the utility to the building. This is installed with materials and methods as specified by the local electrical ...
Aluminium-magnesium alloys are considered to be very corrosion-resistant, making them suitable for marine applications, but this is only true if the -phase exists as a non-contiguous phase. Alloys with Mg contents below 3% are therefore always corrosion-resistant, with higher contents, appropriate heat treatment must ensure that this phase is ...
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.