ISO 18265: "Metallic materials — Conversion of hardness values" (2013) ASTM E140-12B(2019)e1: "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" (2019)
Download QR code; Print/export Download as PDF; Printable version; In other projects Wikidata item; ... Mohs hardness [1] Vickers hardness (MPa) [1] Brinell hardness
A Rockwell hardness tester. The Rockwell hardness test is a hardness test based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
The unit of hardness given by the test is known as the Vickers Pyramid Number (HV) or Diamond Pyramid Hardness (DPH). The hardness number can be converted into units of pascals, but should not be confused with pressure, which uses the same units. The hardness number is determined by the load over the surface area of the indentation and not the ...
According to the dynamic Leeb principle, the hardness value is derived from the energy loss of a defined impact body after impacting on a metal sample, similar to the Shore scleroscope. The Leeb quotient ( v i , v r ) is taken as a measure of the energy loss by plastic deformation: the impact body rebounds faster from harder test samples than ...
The Barcol hardness test is generally used on soft materials such as rigid plastics. It measures hardness based on indentation of a sharp point with a flat tip. The test is performed using a similar method and indentation device as that used to measure Shore D hardness , however the Shore D indentor has a round tip. [ 4 ]
Vickers hardness test (HV) Knoop hardness test (HK) In microindentation testing, the hardness number is based on measurements made of the indent formed in the surface of the test specimen. The hardness number is based on the applied force divided by the surface area of the indent itself, giving hardness units in kgf/mm 2. Microindentation ...
At such low load, the hardness values are also overestimated for other materials, for example it exceeds 100 GPa for c-BN. [4] Other researchers, while having reproduced the high ReB 2 hardness at low load, reported much lower values of 19–17 GPa at a more conventional load of 3–49 N, that makes ReB 2 a hard, but not a superhard material.