Calcium oxide (formula: Ca O), commonly known as quicklime or burnt lime, is a widely used chemical compound. It is a white, caustic , alkaline , crystalline solid at room temperature . The broadly used term lime connotes calcium-containing inorganic compounds , in which carbonates , oxides , and hydroxides of calcium, silicon , magnesium ...
The cement chemist notation is not restricted to cement applications but is in fact a more general notation of oxide chemistry applicable to other domains than cement chemistry sensu stricto. For instance, in ceramics applications, the kaolinite formula can also be written in terms of oxides, thus the corresponding formula for kaolinite,
To convert the oxide notation in LDH formula, the mass balance in the system has to respect the principle of the conservation of matter. Oxide ions (O 2−) and water are transformed into 2 hydroxide anions (OH −) according to the acid-base reaction between H 2 O and O 2− (a strong base) as typically exemplified by the quicklime slaking ...
Calcium aluminates phase diagram Crystal structure of dodecacalcium hepta-aluminate, 12CaO·7Al 2 O 3 (C 12 A 7). [1] Calcium aluminates are a range of materials [2] obtained by heating calcium oxide and aluminium oxide together at high temperatures. They are encountered in the manufacture of refractories and cements.
The root of the word calcination refers to its most prominent use, which is to remove carbon from limestone (calcium carbonate) through combustion to yield calcium oxide (quicklime). This calcination reaction is CaCO 3 (s) → CaO(s) + CO 2 (g). Calcium oxide is a crucial ingredient in modern cement, and is also used as a chemical flux in smelting.
In keeping with its high basicity, tricalcium aluminate reacts most strongly with water of all the calcium aluminates, and it is also the most reactive of the Portland clinker phases. Its hydration to phases of the form Ca 2 AlO 3 (OH) · n H 2 O leads to the phenomenon of "flash set" (instantaneous set), and a large amount of heat is generated.
Calcium hydroxide is moderately soluble in water, as seen for many dihydroxides. Its solubility increases from 0.66 g/L at 100 °C to 1.89 g/L at 0 °C. [8] Its solubility product K sp of 5.02 × 10 −6 at 25 °C, [1] its dissociation in water is large enough that its solutions are basic according to the following dissolution reaction:
Pozzolanic reaction is a long term reaction, which involves dissolved silicic acid, water and CaO or Ca(OH) 2 or other pozzolans to form a strong cementation matrix. This process is often irreversible. Sufficient amount of free calcium ion and a high pH of 12 and above is needed to initiate and maintain the pozzolanic reaction. [2]