Spontaneous glass breakage is a phenomenon by which tempered glass may spontaneously break without any apparent reason. The most common causes are: [13] [14] Internal defects within the glass such as nickel sulfide inclusions. Nickel sulfide defects can cause spontaneous breakage of tempered glass years after its manufacturing. [15]
When the glass is cooled quickly (as part of the process) the NiS particle is unable to change back to its original form. Over a certain period of time NiS will slowly convert to the original low temperature structure. This means the NiS increases in size, and the mechanical stresses caused by this cause the tempered pane to shatter, for no ...
Prince Rupert's drops. Prince Rupert's drops (also known as Dutch tears or Batavian tears) [1] [2] are toughened glass beads created by dripping molten glass into cold water, which causes it to solidify into a tadpole-shaped droplet with a long, thin tail.
Annealing is a process of slowly cooling hot glass objects after they have been formed, to relieve residual internal stresses introduced during manufacture. Especially for smaller, simpler objects, annealing may be incidental to the process of manufacture, but in larger or more complex products it commonly demands a special process of annealing in a temperature-controlled kiln known as a lehr. [1]
Safety glass is glass with additional safety features that make it less likely to break, or less likely to pose a threat when broken. Common designs include toughened glass (also known as tempered glass), laminated glass , and wire mesh glass (also known as wired glass).
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Soda–lime glass (for containers) [2] Borosilicate (low expansion, similar to Pyrex, Duran) Glass wool (for thermal insulation) Special optical glass (similar to Lead crystal) Fused silica Germania glass Germanium selenide glass Chemical composition, wt% 74 SiO 2, 13 Na 2 O, 10.5 CaO, 1.3 Al 2 O 3, 0.3 K 2 O, 0.2 SO 3, 0.2 MgO, 0.01 TiO 2, 0. ...
Glass disease, also referred to as sick glass or glass illness, is a degradation process of glass that can result in weeping, crizzling, spalling, cracking and fragmentation. [ 1 ] [ 2 ] Glass disease is caused by an inherent instability in the chemical composition of the original glass formula. [ 3 ]