It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility. [1] Alternate names and designations include AlSi1MgMn, 3.2315, H30, and A96082. The alloy and its various tempers are covered by the following standards: [2] EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate.
Most strength is recovered in the first few days to a few weeks. Nevertheless, the Aluminum Design Manual (Aluminum Association) recommends the design strength of the material adjacent to the weld to be taken as 165 MPa/24000 PSI without proper heat treatment after the welding. Typical filler material is 4043 or 5356.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
Aluminium oxynitride has the following mechanical properties: [2] Compressive strength 2.68 GPa; Flexural strength 0.38–0.7 GPa; Fracture toughness 2.0 MPa·m 1/2; Knoop hardness 1800 kg/mm 2 (0.2 kg load) Poisson ratio 0.24; Shear modulus 135 GPa; Young's modulus 334 GPa
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards (from any mixture of ASTM, EN, ISO, and national standard bodies), 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy ...