The difference between 304, 304H, and 304L is the carbon content, which is < 0.08, < 0.1, and < 0.035% respectively (also see UNS designations S30400, S30409, & S30403 respectively). 304 has both the H=High and the L=Low carbon variants.
Type 304LN—same as 304L, but also nitrogen is added to obtain a much higher yield and tensile strength than 304L. Type 305—same as 304, but with more nickel to decrease work hardening. Type 308—used as the filler metal when welding 304. Type 309—better temperature resistance than 304, also sometimes used as filler metal when welding ...
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.
Sulfuric acid is one of the most-produced industrial chemicals. At room temperature, type 304 stainless steel is only resistant to 3% acid, while type 316 is resistant to 3% acid up to 50 °C (120 °F) and 20% acid at room temperature. Thus type 304 SS is rarely used in contact with sulfuric acid.
The examples and perspective in this article deal primarily with Europe and do not represent a worldwide view of the subject. You may improve this article, discuss the issue on the talk page, or create a new article, as appropriate.
They are more homogeneous than stainless than other high alloy steels, having carbide only in very small inclusions in the iron. The bulk material is a little bit harder than standard stainless steel such as St-304 (high-end alloys excluded), allowing them to hold a sharper and more acute edge without bending over in contact with hard materials.
304 stainless steel is a common choice of a stainless steel. 304L stainless steel, a low-carbon variant of 304 steel, is used for ultra-high vacuum systems. 316L stainless steel a low-carbon and low-magnetic stainless steel, used in accelerator technologies. 347 stainless steel does not accept high polish. 321 stainless steel is chosen when low ...
Schematic of VAR apparatus. The alloy to undergo VAR is formed into a cylinder typically by vacuum induction melting (VIM) or ladle refining (airmelt). This cylinder, referred to as an electrode is then put into a large cylindrical enclosed crucible and brought to a metallurgical vacuum (0.001–0.1 mmHg or 0.1–13.3 Pa).