A material property is an intensive property of a material, i.e., a physical property or chemical property that does not depend on the amount of the material. These quantitative properties may be used as a metric by which the benefits of one material versus another can be compared, thereby aiding in materials selection.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
The strength of materials is determined using various methods of calculating the stresses and strains in structural members, such as beams, columns, and shafts. The methods employed to predict the response of a structure under loading and its susceptibility to various failure modes takes into account the properties of the materials such as its yield strength, ultimate strength, Young's modulus ...
Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%. ASTM A992 is currently the most available steel type for structural wide-flange beams.
Magnesium casting proof stress is typically 75–200 MPa, tensile strength 135–285 MPa and elongation 2–10%. Typical density is 1.8 g/cm 3 and Young's modulus is 42 GPa. [5]
For iron, aluminium, and copper alloys, is typically 0.4 times the ultimate tensile strength. Maximum typical values for irons are 170 MPa (24 ksi), aluminums 130 MPa (19 ksi), and coppers 97 MPa (14 ksi). [2] Note that these values are for smooth "un-notched" test specimens.
A bolt with property class 12.9 has a tensile strength of 1200 MPa (1 MPa = 1 N/mm 2) or 1.2 kN/mm 2 and the yield strength is 0.90 times tensile strength, 1080 MPa in this case. A bolt with property class 4.6 has a tensile strength of 400 MPa (1 MPa = 1 N/mm 2 ) or 0.4 kN/mm 2 and yield strength is 0.60 times tensile strength, 240 MPa in this ...