The index n usually lies between the values of 2, for fully strain hardened materials, and 2.5, for fully annealed materials. It is roughly related to the strain hardening coefficient in the equation for the true stress-true strain curve by adding 2. [1] Note, however, that below approximately d = 0.5 mm (0.020 in) the value of n can surpass 3.
The strain hardening exponent (also called the strain hardening index), usually denoted , is a measured parameter that quantifies the ability of a material to become stronger due to strain hardening. Strain hardening (work hardening) is the process by which a material's load-bearing capacity increases during plastic (permanent) strain , or ...
For strain less than the ultimate tensile strain, the increase of work-hardening rate in this region will be greater than the area reduction rate, thereby make this region harder to deform than others, so that the instability will be removed, i.e. the material increases in homogeneity before reaching the ultimate strain.
where is the volume fraction of the fibers in the composite (and is the volume fraction of the matrix).. If it is assumed that the composite material behaves as a linear-elastic material, i.e., abiding Hooke's law = for some elastic modulus of the composite and some strain of the composite , then equations 1 and 2 can be combined to give
In mechanics, strain is defined as relative deformation, compared to a reference position configuration. Different equivalent choices may be made for the expression of a strain field depending on whether it is defined with respect to the initial or the final configuration of the body and on whether the metric tensor or its dual is considered.
Strain gauges can be used to experimentally determine the deformation of a physical part. A commonly used type of strain gauge is a thin flat resistor that is affixed to the surface of a part, and which measures the strain in a given direction. From the measurement of strain on a surface in three directions the stress state that developed in ...
The figure also shows the effect of increased strain rate generally increasing the critical resolved shear stress for a constant temperature as this increases the dislocation density in the material. Note that for intermediate temperatures, i.e. region II, there is a region where the strain rate has no effect on the stress.
Strain energy release rate per unit fracture surface area is calculated by J-integral method which is a contour path integral around the crack tip where the path begins and ends on either crack surfaces. J-toughness value signifies the resistance of the material in terms of amount of stress energy required for a crack to grow.