Lime softening (also known as lime buttering, lime-soda treatment, or Clark's process) [1] is a type of water treatment used for water softening, which uses the addition of limewater (calcium hydroxide) to remove hardness (deposits of calcium and magnesium salts) by precipitation.
He became known for the discovery of the phosphate of soda, and the process of lime softening of hard water the 'Clark process'. A Clark degree (°Clark) of water hardness is defined as one grain (64.8 mg) of CaCO 3 per Imperial gallon (4.55 litres) of water, equivalent to 14.254 ppm. and 10^5 parts of water
Water softening is the removal of calcium, magnesium, and certain other metal cations in hard water. The resulting soft water requires less soap for the same cleaning effort, as soap is not wasted bonding with calcium ions.
Precipitative softening: [4]: 13.12–13.58 Water rich in hardness (calcium and magnesium ions) is treated with lime (calcium oxide) and/or soda-ash (sodium carbonate) to precipitate calcium carbonate out of solution utilising the common-ion effect. Electrodeionization: [9] Water is passed between a positive electrode and a negative electrode.
An example batch calculation may be demonstrated here. The desired glass composition in wt% is: 67 SiO 2, 12 Na 2 O, 10 CaO, 5 Al 2 O 3, 1 K 2 O, 2 MgO, 3 B 2 O 3, and as raw materials are used sand, trona, lime, albite, orthoclase, dolomite, and borax. The formulas and molar masses of the glass and batch components are listed in the following ...
Soda lime canister used in anaesthetic machines to act as a carbon dioxide scrubber. Soda lime, a mixture of sodium hydroxide (NaOH) and calcium oxide (CaO), is used in granular form within recirculating breathing environments like general anesthesia and its breathing circuit, submarines, rebreathers, and hyperbaric chambers and underwater habitats.
Ordinary soda-lime glass, used in windows and drinking containers, is created by the addition of sodium carbonate and lime (calcium oxide) to silicon dioxide. Without these additives, silicon dioxide would require very high temperature to obtain a melt, and subsequently (with slow cooling) a glass.
The theoretical heat (the standard enthalpy) of reaction required to make high-calcium lime is around 3.15 MJ per kg of lime, so the batch kilns were only around 20% efficient. The key to development in efficiency was the invention of continuous kilns, avoiding the wasteful heat-up and cool-down cycles of the batch kilns.