Therefore, when concreting at cold temperature cannot be avoided, it is essential to have a minimum curing time at a temperature sufficiently above the freezing point of the concrete pore water, so that the early strength of concrete is high enough to resist the inner tensile stress caused by water freezing. [5]
The addition of an accelerator speeds the setting time and thus curing starts earlier. [1] This allows concrete to be placed in winter with reduced risk of frost damage. [2] Concrete is damaged if it does not reach a strength of 500 pounds per square inch (3.4 MPa) before freezing. [3] Typical cement accelerators are calcium nitrate (Ca(NO 3)
3 Code of Practices for plain and reinforced concrete etc. IS 456 – 2000 4 Methods of sampling and analysis of concrete IS 1199 – 1959 5 Recommended Guide Lines for Concrete Mix Design IS 10262 – 1982 (F) Curing Compound; 1 Standard test method for water retention & daylight reflection test on concrete. ASTM-C-156809
To limit self-desiccation shrinkage during hardening, SAPs were added as an internal curing agent in cementitious systems with a low water-to-binder ratio. Aside from reducing autogenous shrinkage, SAPs may be added to cementitious materials to improve freeze-thaw resistance and induce self-sealing and self-healing properties. In terms of the ...
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
"Freeze-Thaw resistance". Polymers in Concrete. CRC Press. pp. 40–42. ISBN 9780849348150. J. Marchand; Michel Pigeon; M. Setzer (1997). Freeze–thaw Durability of Concrete. Proceedings of the International Workshop in the Resistance of Concrete to Scaling Due to Freezing in the Presence of De-icing Salts, Sainte-Foy, Québec, Canada.
Concrete must be kept moist during curing in order to achieve optimal strength and durability. [75] During curing hydration occurs, allowing calcium-silicate hydrate (C-S-H) to form. Over 90% of a mix's final strength is typically reached within four weeks, with the remaining 10% achieved over years or even decades. [ 76 ]
A pervious concrete street in 2005. Pervious concrete (also called porous concrete, permeable concrete, no fines concrete and porous pavement) is a special type of concrete with a high porosity used for concrete flatwork applications that allows water from precipitation and other sources to pass directly through, thereby reducing the runoff from a site and allowing groundwater recharge.