6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061.The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.
The temper designation follows the cast or wrought designation number with a dash, a letter, and potentially a one to three digit number, e.g. 6061-T6. The definitions for the tempers are: [5] [6]-F : As fabricated-H : Strain hardened (cold worked) with or without thermal treatment -H1 : Strain hardened without thermal treatment
Alloys with higher copper content (alloyings 6061, 6056, 6013) are mainly used in aviation. Iron occurs in all aluminium alloys as an impurity in quantities of 0.05-0.5%. It forms the phases Al8Fe2Si, Al5FeSi and Al8FeMg3Si6, which are all thermally stable, but undesirable because they brittle the material. Silicon surpluses are also used to ...
6005A aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is closely related, but not identical, to 6005 aluminium alloy.