Butt welding is usually performed using one of several methods. The first, and most common, is butt welding or butt fusion, which is a type of hot plate welding. This technique involves heating two planed surfaces of thermoplastic material (typically polyethylene) against a heated surface. After a specified amount of time, the heating plate is ...
With speed welding, the plastic welder, similar to a soldering iron in appearance and wattage, is fitted with a feed tube for the plastic weld rod. The speed tip heats the rod and the substrate, while at the same time it presses the molten weld rod into position. A bead of softened plastic is laid into the joint, and the parts and weld rod fuse.
Radio-frequency welding, also known as dielectric welding and high-frequency welding, is a plastic welding process that utilizes high-frequency electric fields to induce heating and melting of thermoplastic base materials. [1] The electric field is applied by a pair of electrodes after the parts being joined are clamped together.
Implant induction welding is a joining method used in plastic manufacturing. The welding process uses an induction coil to excite and heat electromagnetically susceptible material at the joint interface and melt the thermoplastic. The susceptible material can be contained in a gasket placed between the welding surface, or within the actual ...
Hot plate welding was first used in the early 1930s for joining PVC. [1] It gained in popularity with the prevalence of polyolefins, which are difficult to adhesively bond. By the 1960s, it was among the most widely used plastic welding methods. [2] Hot plate welding was used for pipelines and appliances as well as injection moldings.
Solvent bonding differs from other plastic welding processes in that heating energy is generated by the chemical reaction between the solvent and thermoplastic, and cooling occurs during evaporation of the solvent. [5] Solvent bonding can be performed using a liquid or gaseous solvent.
A common post-extrusion process for plastic sheet stock is thermoforming, where the sheet is heated until soft (plastic), and formed via a mold into a new shape. When vacuum is used, this is often described as vacuum forming. Orientation (i.e. ability/ available density of the sheet to be drawn to the mold which can vary in depths from 1 to 36 ...
Spin welding creates a clean and sound weld joint that requires little post processing. [3] Due to this most parts being welded are in the final stages of production, or are in final assembly. The first known application of spin welding was in the assembly of compasses, however spin welding has become used in a wide variety of products.