The downward curve after saturation, along with the lower return curve, form the main loop. The intercepts h c and m rs are the coercivity and saturation remanence. Magnetic hysteresis occurs when an external magnetic field is applied to a ferromagnet such as iron and the atomic dipoles align themselves with it.
Calculated magnetization curve for a superconducting slab, based on Bean's model. The superconducting slab is initially at H = 0. Increasing H to critical field H* causes the blue curve; dropping H back to 0 and reversing direction to increase it to -H* causes the green curve; dropping H back to 0 again and increase H to H* causes the orange curve.
The curves form a hysteresis loop. Hysteresis is the dependence of the state of a system on its history. For example, a magnet may have more than one possible magnetic moment in a given magnetic field, depending on how the field changed in the past. Plots of a single component of the moment often form a loop or hysteresis curve, where there are ...
Saturation is most clearly seen in the magnetization curve (also called BH curve or hysteresis curve) of a substance, as a bending to the right of the curve (see graph at right). As the H field increases, the B field approaches a maximum value asymptotically , the saturation level for the substance.
The downward curve after saturation, along with the lower return curve, form the main loop. The intercepts h c and m rs are the coercivity and saturation remanence . When ferrimagnets are exposed to an external magnetic field, they display what is called magnetic hysteresis , where magnetic behavior depends on the history of the magnet.
Compass needles in the Northern Hemisphere point toward the magnetic North Pole, although the exact location of it changes from time to time as the contours of Earth’s magnetic field also change.
The default definition of magnetic remanence is the magnetization remaining in zero field after a large magnetic field is applied (enough to achieve saturation). [1] The effect of a magnetic hysteresis loop is measured using instruments such as a vibrating sample magnetometer ; and the zero-field intercept is a measure of the remanence.
Hysteresis loop Induction B as function of field strength H for H varying between H min and H max; for ferromagnetic material the B has different values for H going up and down, therefore a plot of the function forms a loop instead of a curve joining two points; for perminvar type materials, the loop is a "rectangle" (Domain Structure of Perminvar Having a Rectangular Hysteresis Loop, Williams ...