Ads
related to: strength of stainless steel chain for menetsy.com has been visited by 1M+ users in the past month
- Bestsellers
Shop Our Latest And Greatest
Find Your New Favorite Thing
- Personalized Gifts
Shop Truly One-Of-A-Kind Items
For Truly One-Of-A-Kind People
- Free Shipping Orders $35+
On US Orders From The Same Shop.
Participating Shops Only. See Terms
- Editors' Picks
Daily Discoveries Curated By
Our Resident Statement Makers
- Bestsellers
Search results
Results from the WOW.Com Content Network
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an alloy of iron that is resistant to rusting and corrosion. It contains iron with chromium and other elements such as molybdenum , carbon , nickel and nitrogen depending on its specific use and cost.
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
17-4 stainless steel can be heat treated to approximately 44 Rc, [1] and an ultimate tensile strength of 1,300 MPa (190,000 psi). Its density ranges from 7,800 to 7,900 kg/m 3 (0.282 to 0.284 lb/cu in), and its modulus of elasticity ranges from 197 to 207 GPa (28.5 × 10 ^ 6 to 30.0 × 10 ^ 6 psi).
Stainless steel is used in a variety of applications in dentistry. It is common to use stainless steel in many instruments that need to be sterilized, such as needles, [42] endodontic files in root canal therapy, metal posts in root canal-treated teeth, temporary crowns and crowns for deciduous teeth, and arch wires and brackets in orthodontics ...
440C (UNS designation S44004) is a martensitic 400 series stainless steel, [1] and has the highest carbon content of the 400 stainless steel series. It can be heat treated to reach hardness of 58 to 60 HRC. It can be used to make rolling contact stainless bearings, e.g. ball bearings and roller bearings. It is also used to make knife blades.