An anisotropic wet etch on a silicon wafer creates a cavity with a trapezoidal cross-section. The bottom of the cavity is a {100} plane (see Miller indices), and the sides are {111} planes. The blue material is an etch mask, and the green material is silicon.
Anisotropy (/ ˌænaɪˈsɒtrəpi, ˌænɪ -/) is the structural property of non-uniformity in different directions, as opposed to isotropy. An anisotropic object or pattern has properties that differ according to direction of measurement. For example, many materials exhibit very different physical or mechanical properties when measured along ...
Deep reactive-ion etching. Deep reactive-ion etching (DRIE) is a special subclass of reactive-ion etching (RIE). It enables highly anisotropic etch process used to create deep penetration, steep-sided holes and trenches in wafers /substrates, typically with high aspect ratios. It was developed for microelectromechanical systems (MEMS), which ...
Metal Assisted Chemical Etching (also known as MACE) is the process of wet chemical etching of semiconductors (mainly silicon) with the use of a metal catalyst, usually deposited on the surface of a semiconductor in the form of a thin film or nanoparticles. The semiconductor, covered with the metal is then immersed in an etching solution ...
Isotropic etching. Isotropic etching is a method commonly used in semiconductors to remove material from a substrate via a chemical process using an etchant substance. The etchant may be in liquid-, gas- or plasma -phase, [1] although liquid etchants such as buffered hydrofluoric acid (BHF) for silicon dioxide etching are more often used.
A reactive-ion etching setup in a laboratory cleanroom. Reactive-ion etching (RIE) is an etching technology used in microfabrication. RIE is a type of dry etching which has different characteristics than wet etching. RIE uses chemically reactive plasma to remove material deposited on wafers. The plasma is generated under low pressure (vacuum ...
This is known as anisotropic etching and one of the most common examples is the etching of silicon in KOH (potassium hydroxide), where Si <111> planes etch approximately 100 times slower than other planes (crystallographic orientations). Therefore, etching a rectangular hole in a (100)-Si wafer results in a pyramid shaped etch pit with 54.7 ...
Bulk micromachining starts with a silicon wafer or other substrates which is selectively etched, using photolithography to transfer a pattern from a mask to the surface. Like surface micromachining, bulk micromachining can be performed with wet or dry etches, although the most common etch in silicon is the anisotropic wet etch.