Barcol hardness is measured on a scale from 0 to 100 with the typical range being between 50B and 90B. A measurement of 60B is roughly equivalent to a Shore hardness of 80D or a Rockwell hardness M100. [4] [6] As defined in ASTM D 2583 the scale divisions from 0-100 should each indicate a depth of 0.0076 mm or the equivalent 0.0003 inches. [7]
In the 1930s, national studies demonstrated the Deval test did not correlate with the service record of sampled rock altogether, while an LA loss rating of less than 40% was a reliable indicator of quality. [9] The federal standard for LA abrasion testing was formally adopted by the ASTM in 1937. [10]
Epoxy value derives from the Epoxy equivalent weight (EEW) or Weight Per Epoxide (WPE) and is a measure of the epoxy content of an epoxy resin or epoxy reactive diluent, or glycidyl ether. [1] This is an important parameter as it allows determination of the correct mix ratio of an epoxy system with a curing agent. [ 2 ]
Pitting resistance equivalent number (PREN) is a predictive measurement of a stainless steel's resistance to localized pitting corrosion based on its chemical composition. In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride .
The Janka hardness test results tabulated below followed ASTM D 1037-12 testing methods. Lumber stocks tested range from 1" to 2" (25–50 mm) thick. The tabulated Janka hardness numbers are an average. There is a standard deviation associated with each species, but these values are not given. [citation needed] No testing was done on actual ...
The VPAM scale as of 2009 runs from 1 to 14, with 1-5 being soft armor, and 6-14 being hard armor. [1] Tested armor must withstand three hits, spaced 120 mm (4.7 inches) apart, of the designated test threat with no more than 25 mm (0.98 inches) of back-face deformation in order to pass.
The longer it takes, the higher the viscosity and thus the higher the SAE code. Larger numbers are thicker. J300 specifies a viscosity range for each non-winter grade, with higher grade numbers corresponding to higher viscosities. In addition, a minimum viscosity measured at a high temperature and high-shear rate (HTHS, ASTM D4683) is also ...
The sand equivalent test quantifies the relative abundance of sand versus clay in soil. It is measured by standardized test methods such as ASTM D2419, AASHTO T176, and EN 933–8. [ 1 ] The test is used to qualify aggregates for applications where sand is desirable but fines and dust are not.