The blast furnaces used in the Imperial Smelting Process ("ISP") were developed from the standard lead blast furnace, but are fully sealed. [79] This is because the zinc produced by these furnaces is recovered as metal from the vapor phase, and the presence of oxygen in the off-gas would result in the formation of zinc oxide. [79]
Molten pig iron (sometimes referred to as "hot metal") from a blast furnace is poured into a large refractory-lined container called a ladle. The metal in the ladle is sent directly for basic oxygen steelmaking or to a pretreatment stage where sulfur, silicon, and phosphorus are removed before charging the hot metal into the converter.
The hot blast pumps hot air into the blast furnace. The hot blast temperature ranges from 900 to 1,300 °C (1,650 to 2,370 °F) depending on the design and condition. Oil, tar , natural gas, powdered coal and oxygen can be injected to combine with the coke to release additional energy and increase the percentage of reducing gases present ...
The configuration of iron ore pellets as packed spheres in the blast furnace allows air to flow between the pellets, decreasing the resistance to the air that flows up through the layers of material during the smelting. The configuration of iron ore powder in a blast furnace is more tightly-packed and restricts the air flow.
By this method he hoped to cause the new process to gain in standing and market share. [ 10 ] He realised that the technical problem was due to impurities in the iron and concluded that the solution lay in knowing when to turn off the flow of air in his process so that the impurities were burned off but just the right amount of carbon remained.
The Chinese are thought to have skipped the bloomery process completely, starting with the blast furnace and the finery forge to produce wrought iron; by the fifth century BC, metalworkers in the southern state of Wu had invented the blast furnace and the means to both cast iron and to decarburize the carbon-rich pig iron produced in a blast ...
The process starts by charging solid sinter and heated coke into the top of the blast furnace. Preheated air at 190 to 1,050 °C (370 to 1,920 °F) is blown into the bottom of the furnace. Zinc vapour and sulfides leave through the top and enter the condenser. Slag and lead collect at the bottom of the furnace and are tapped off regularly.
The Scrantons instead used the new "hot blast method," developed in Scotland in 1828. [7] The hot blast method solved the problem of impurities from the coke, by burning them off. The Scrantons also experimented with anthracite to make steel, rather than charcoal or bituminous coal. [9]