Precipitation hardening (also called age hardening) is a process where a second phase that begins in solid solution with the matrix metal is precipitated out of solution with the metal as it is quenched, leaving particles of that phase distributed throughout to cause resistance to slip dislocations. This is achieved by first heating the metal ...
To examine a piece of steel, obtain a hand file and file an edge of the selected metal. If the piece of steel has not undergone the hardening process, the metal file should easily 'bite' into the sample. If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect.
A forming limit diagram, also known as a forming limit curve, is used in sheet metal forming for predicting forming behavior of sheet metal. [1] [2] The diagram attempts to provide a graphical description of material failure tests, such as a punched dome test. In order to determine whether a given region has failed, a mechanical test is performed.
At 0-D there is precipitate and solid solution strengthening with particulates strengthening structure, at 1-D there is work/forest hardening with line dislocations as the hardening mechanism, and at 2-D there is grain boundary strengthening with surface energy of granular interfaces providing strength improvement.
The hardenability of a ferrous alloy is measured by a Jominy test: a round metal bar of standard size (indicated in the top image) is transformed to 100% austenite through heat treatment, and is then quenched on one end with room-temperature water. The cooling rate will be highest at the end being quenched, and will decrease as distance from ...
Induction hardening is a type of surface hardening in which a metal part is induction-heated and then quenched. The quenched metal undergoes a martensitic transformation, increasing the hardness and brittleness of the part. Induction hardening is used to selectively harden areas of a part or assembly without affecting the properties of the part ...
Austempering is a hardening process that is used on iron-based metals to promote better mechanical properties. The metal is heated into the austenite region of the iron- cementite phase diagram and then quenched in a salt bath or other heat extraction medium that is between temperatures of 300–375 °C (572–707 °F).
The hamon of a blade is created during the quenching process (yakiire). During the differential heat treatment, the clay coating on the back of the sword reduces the cooling speed of the red-hot metal when it is plunged into the water and allows the steel to turn into pearlite, a soft structure consisting of cementite and ferrite (iron ...