Soldering copper pipes using a propane torch and a lead-free solder. Solder is a metallic material that is used to connect metal workpieces. The choice of specific solder alloys depends on their melting point, chemical reactivity, mechanical properties, toxicity, and other properties. Hence a wide range of solder alloys exist, and only major ...
When lead-free solder is used in wave soldering, a slightly modified solder pot may be desirable (e.g. titanium liners or impellers) to reduce maintenance cost due to increased tin-scavenging of high-tin solder. Lead-free solder is prohibited in critical applications, such as aerospace, military and medical projects, because joints are likely ...
Additionally, tin is a more corrosive metal, and can eventually lead to the failure of solder baths [clarification needed]. [36] Lead-free construction has also extended to components, pins, and connectors. Most of these pins used copper frames, and either lead, tin, gold or other finishes. Tin finishes are the most popular of lead-free finishes.
The solder grade used for leadworking is plumber's solder (80% lead / 20% tin). [i] Although this is thought of as a high melting point solder amongst lead-tin solders, the solidus is relatively constant for all of these solders and it is the liquidus which climbs from the eutectic point at Sn 63% / Pb 37%.
Solderability when using lead-free alloys can differ significantly from solderability when using lead based alloys. Noble metals may be easy to solder but they have brittle joints. The metals in the good category require a large amount of heat therefore oxidation is an issue. To overcome this a flux is required.
The most common dip soldering operations use zinc-aluminum and tin-lead solders. Solder pot metal: cast iron or steel, electrically heated. Bath temperature: 220 to 260 °C (for binary tin-lead alloys) or 350 to 400 °C (for lead-free alloys) Solder composition: 60% Sn, 40% Pb or eutectic alloy.
The more common lead-free solder systems have a higher melting point, e.g. a 30 °C typical difference for tin-silver-copper alloys, but wave soldering temperatures are approximately the same at ~255 °C; [47] however at this temperature most typical lead-free solders have longer wetting times than eutectic Pb/Sn 37:63 solder. [49]