Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an electrochemical process in which one metal corrodes preferentially when it is in electrical contact with another, in the presence of an electrolyte.
The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the difference in ...
Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [1] [2]
Galvanic corrosion is the electrochemical erosion of metals. Corrosion occurs when two dissimilar metals are in contact with each other in the presence of an electrolyte, such as salt water. This forms a galvanic cell, with hydrogen gas forming on the more noble (less active) metal. The resulting electrochemical potential then develops an ...
Over time the galvanic anode continues to corrode, consuming the anode material until eventually it must be replaced. Galvanic or sacrificial anodes are made in various shapes and sizes using alloys of zinc, magnesium, and aluminum. ASTM International publishes standards on the composition and manufacturing of galvanic anodes. [10] [11] [12]
The corrosion protection is primarily due to the anodic potential dissolution of zinc versus iron. Zinc acts as a sacrificial anode for protecting iron (steel). While steel is close to -400 mV, depending on alloy composition, electroplated zinc is much more anodic with -980 mV. Steel is preserved from corrosion by cathodic protection. Alloying ...
Bimetallic corrosion. Galvanic corrosion (also called bimetallic corrosion) is an electrochemical process in which one metal (more active one) corrodes preferentially when it is in electrical contact with another dissimilar metal, in the presence of an electrolyte.
Crevice corrosion refers to corrosion occurring in occluded spaces such as interstices in which a stagnant solution is trapped and not renewed. [1] These spaces are generally called crevices. Examples of crevices are gaps and contact areas between parts, under gaskets or seals, inside cracks and seams, spaces filled with deposits and under ...