Prince Rupert's drops have remained a scientific curiosity for nearly 400 years due to two unusual mechanical properties: [4] when the tail is snipped, the drop disintegrates explosively into powder, whereas the bulbous head can withstand compressive forces of up to 664,300 newtons (67,740 kg f).
Spontaneous glass breakage is a phenomenon by which tempered glass may spontaneously break without any apparent reason. The most common causes are: [13] [14] Internal defects within the glass such as nickel sulfide inclusions. Nickel sulfide defects can cause spontaneous breakage of tempered glass years after its manufacturing. [15]
[4] The mechanisms controlling formation of volcanic glass are further illustrated by the two forms of basaltic glass, tachylite and sideromelane. Tachylite is opaque to transmitted light because of the abundance of tiny oxide mineral crystals suspended in the glass. Sideromelane is partially transparent because it contains much fewer crystals.
Annealing is a process of slowly cooling hot glass objects after they have been formed, to relieve residual internal stresses introduced during manufacture. Especially for smaller, simpler objects, annealing may be incidental to the process of manufacture, but in larger or more complex products it commonly demands a special process of annealing in a temperature-controlled kiln known as a lehr. [1]
A 4-year-old accidentally knocked over and shattered a 3,500-year-old Bronze Age jar during a visit to the Hecht Museum at the University of Haifa in Israel on Friday.. The museum said the ...
Unless stated otherwise, the properties of fused silica (quartz glass) and germania glass are derived from the SciGlass glass database by forming the arithmetic mean of all the experimental values from different authors (in general more than 10 independent sources for quartz glass and T g of germanium oxide glass). The list is not exhaustive.
When the glass is cooled quickly (as part of the process) the NiS particle is unable to change back to its original form. Over a certain period of time NiS will slowly convert to the original low temperature structure. This means the NiS increases in size, and the mechanical stresses caused by this cause the tempered pane to shatter, for no ...
Ninja rocks take advantage of the physical properties of tempered glass, disrupting surface compressive stress and causing the glass to shatter. Tempered glass, which is used for the side windows of most vehicles, is manufactured with an extremely high surface compressive stress and high internal tensile stress. This gives it strength and ...