Portland cement is the most common type of cement and is a general purpose cement. The product is made with a combination of calcium, silicon, aluminum, iron, and other ingredients.
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
Portland cement blends are often available as inter-ground mixtures from cement producers, but similar formulations are often also mixed from the ground components at the concrete mixing plant. Portland blast-furnace slag cement , or blast furnace cement (ASTM C595 and EN 197-1 nomenclature respectively), contains up to 95% ground granulated ...
The water-cement ratio of the fresh concrete mix is one of the main, if not the most important, factors determining the quality and properties of hardened concrete, as it directly affects the concrete porosity, and a good concrete is always a concrete as compact and as dense as possible.
Portland cement is the most common type of cement in general use around the world as a basic ingredient of concrete, mortar, stucco, and non-specialty grout. It was developed from other types of hydraulic lime in England in the early 19th century by Joseph Aspdin , and is usually made from limestone .
Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water. This reaction typically is expressed as: 2 Ca 3 SiO 5 + 7 H 2 O → 3 CaO · 2 SiO 2 · 4 H 2 O + 3 Ca(OH) 2 + 173.6 kJ. also written in cement chemist notation, (CCN) as: 2 C 3 S + 7 H → C 3 S 2 H 4 + 3 CH + heat
High-strength concrete has a compressive strength greater than 40 MPa (6000 psi). In the UK, BS EN 206-1 [2] defines High strength concrete as concrete with a compressive strength class higher than C50/60. High-strength concrete is made by lowering the water-cement (W/C) ratio to 0.35 or lower.
Because several specific formulas are included in the HPFRCC class, their physical compositions vary considerably. However, most HPFRCCs include at least the following ingredients: fine aggregates, a superplasticizer, polymeric or metallic fibers, cement, and water. Thus the principal difference between HPFRCC and typical concrete composition ...