Brass is more malleable than bronze or zinc. The relatively low melting point of brass (900 to 940 °C; 1,650 to 1,720 °F, depending on composition) and its flow characteristics make it a relatively easy material to cast. By varying the proportions of copper and zinc, the properties of the brass can be changed, allowing hard and soft brasses.
The Gmelin rare earths handbook lists 1522 °C and 1550 °C as two melting points given in the literature, the most recent reference [Handbook on the chemistry and physics of rare earths, vol.12 (1989)] is given with 1529 °C.
Bronze is an alloy consisting primarily of copper, commonly with about 12–12.5% tin and often with the addition of other metals (including aluminium, manganese, nickel, or zinc) and sometimes non-metals (such as phosphorus) or metalloids (such as arsenic or silicon).
The melting point (or, rarely, liquefaction point) of a substance is the temperature at which it changes state from solid to liquid. At the melting point the solid and liquid phase exist in equilibrium. The melting point of a substance depends on pressure and is usually specified at a standard pressure such as 1 atmosphere or 100 kPa.
The metals of antiquity generally have low melting points, with iron being the exception. Mercury melts at −38.829 °C (−37.89 °F) [21] (being liquid at room temperature). Tin melts at 231 °C (449 °F) [21] Lead melts at 327 °C (621 °F) [21] Silver at 961 °C (1763 °F) [21] Gold at 1064 °C (1947 °F) [21] Copper at 1084 °C (1984 °F ...
Bell metal or bell bronze is an alloy used for making bells and related instruments, such as cymbals. It is a form of bronze with a higher tin content than most other bronzes, usually in approximately a 4:1 ratio of copper to tin (typically, 78% copper, 22% tin by mass).
A material property is an intensive property of a material, i.e., a physical property or chemical property that does not depend on the amount of the material. These quantitative properties may be used as a metric by which the benefits of one material versus another can be compared, thereby aiding in materials selection.
Gunmetal ingot is a related alloy in which the zinc is replaced by 2% lead; this makes the alloy easier to cast but it has less strength. [2]Modified gunmetal contains lead in addition to the zinc; it is typically composed of 86% copper, 9.5% tin, 2.5% lead, and 2% zinc.