Vitrified clay pipe (VCP) is pipe made from a blend of clay and shale that has been subjected to high temperature to achieve vitrification, which results in a hard, inert ceramic. VCP is commonly used in gravity sewer collection mains because of its long life and resistance to almost all domestic and industrial sewage , particularly the ...
Underglaze transfers are a technique that involves screenprinting or free handing a pattern onto a transfer paper (often rice paper or newspaper) which is then placed, dampened, and burnished onto the surface of a leather-hard piece of clay (similar to how a lick-and-stick tattoo might be applied). [21]
[contradictory] This type of clay is water-soluble and unstable. Earthenware is clay that has been fired between 1000–1200°C or 1832°–2192°F. The firing makes the clay water insoluble but does not allow the formation of an extensive glassy or vitreous within the body. Although water-insoluble, the porous body of earthenware allows water ...
A procedure for preparing clay or a clay body by hand: the lump of clay is repeatedly thrown down on a work bench; between each operation the lump is turned and sometimes cut through and rejoined in a different orientation. The object is to disperse the water more uniformly, to remove lamination and to remove air. Whiteware
Glazes need to include a ceramic flux which functions by promoting partial liquefaction in the clay bodies and the other glaze materials. Fluxes lower the high melting point of the glass forms silica, and sometimes boron trioxide. Raw materials for ceramic glazes generally include silica, which will be the main glass former.
Blue glazes were first developed by ancient Mesopotamians to imitate lapis lazuli, which was a highly prized stone. Later, a cobalt blue glaze became popular in Islamic pottery during the Abbasid Caliphate, during which time the cobalt was mined near Kashan , Oman , and Northern Hejaz .
In such cases the first firing for the body, underglaze decoration and glaze is followed by the second firing after the overglaze enamels have been applied. The technique essentially uses powdered glass mixed with coloured pigments, and is the application of vitreous enamel to pottery; enamelled glass is very similar but on glass. Both these ...
Hard-paste porcelain was invented in China, and it was also used in Japanese porcelain.Most of the finest quality porcelain wares are made of this material. The earliest European porcelains were produced at the Meissen factory in the early 18th century; they were formed from a paste composed of kaolin and alabaster and fired at temperatures up to 1,400 °C (2,552 °F) in a wood-fired kiln ...