Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
Schematic and dimensions of a compact tension specimen. A compact tension specimen (CT) is a type of standard notched specimen in accordance with ASTM [1] and ISO [2] standards. Compact tension specimens are used extensively in the area of fracture mechanics and corrosion testing, in order to establish fracture toughness and fatigue crack ...
The Izod impact strength test is an ASTM standard method of ... The dimensions of a standard specimen for ASTM D256 are 63.5 × 12.7 × 3.2 mm (2.5 × 0.5 × 0.125 in ...
According to ASTM A370, [12] the standard specimen size for Charpy impact testing is 10 mm × 10 mm × 55 mm. Subsize specimen sizes are: 10 mm × 7.5 mm × 55 mm, 10 mm × 6.7 mm × 55 mm, 10 mm × 5 mm × 55 mm, 10 mm × 3.3 mm × 55 mm, 10 mm × 2.5 mm × 55 mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for ...
The type of notch introduced to a specimen depends on the material and characterization employed. For standardized testing of fracture toughness by the Charpy impact method, specimen and notch dimensions are most often taken from American standard ASTM E23, or British standard BS EN ISO 148-1:2009.
Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%. ASTM A992 is currently the most available steel type for structural wide-flange beams.
This test is performed on a universal testing machine (tensile testing machine or tensile tester) with a three-point or four-point bend fixture. The main advantage of a three-point flexural test is the ease of the specimen preparation and testing.
The success of a biaxial tensile test is strictly related to the shape of the specimen. [17] The two most used geometries are the square and cruciform shapes. Dealing with fibrous materials or fibres reinforced composites , the fibres should be aligned to the load directions for both classes of specimens, in order to minimize the shear stresses ...