However, it is not beyond doubt that the passage describes deliberate quench-hardening, rather than simply cooling. [8] Likewise, there is a prospect that the Mahabharata refers to the oil-quenching of iron arrowheads, but the evidence is problematic. [9] Pliny the Elder addressed the topic of quenchants, distinguishing the water of different ...
The quenching is required since the material otherwise would start the precipitation already during the slow cooling. This type of precipitation results in few large particles rather than the, generally desired, profusion of small precipitates. Precipitation hardening is one of the most commonly used techniques for the hardening of metal alloys.
Quenching is the process of cooling metal very quickly after heating, thus "freezing" the metal's molecules in the very hard martensite form, which makes the metal harder. Tempering relieves stresses in the metal that were caused by the hardening process; tempering makes the metal less hard while making it better able to sustain impacts without ...
The two important aspects of quenching are the cooling rate and the holding time. The most common practice is to quench into a bath of liquid nitrite-nitrate salt and hold in the bath. Because of the restricted temperature range for processing it is not usually possible to quench in water or brine, but high temperature oils are used for a ...
Unlike differential hardening, where the entire piece is heated and then cooled at different rates, in flame hardening, only a portion of the metal is heated before quenching. This is usually easier than differential hardening, but often produces an extremely brittle zone between the heated metal and the unheated metal, as cooling at the edge ...
Martempering is also known as stepped quenching or interrupted quenching. In this process, steel is heated above the upper critical point (above the transformation range) and then quenched in a hot-oil, molten-salt, or molten-lead bath kept at a temperature of 150-300 °C. The workpiece is held at this temperature above martensite start (Ms ...
The quenching converts the billet's surface layer to martensite, and causes it to shrink. The shrinkage pressurizes the core, helping to form the correct crystal structures. The core remains hot, and austenitic. A microprocessor controls the water flow to the quench box, to manage the temperature difference through the cross-section of the bars.
Steel which has a carbon content greater than ~0.25% can be direct-hardened by heating to around 600°C, and then quickly cooling, often by immersing in water or oil, known as quenching. Hardening is desirable for metal components because it gives increased strength and wear resistance, the tradeoff being that hardened steel is generally more ...