The history of molding sand is difficult to study, as much of the origins of the practice predate writing. Molding sand was used exclusively for bronze casts, which was pioneered by the ancient Chinese. The next major advancement came in India in 500 B.C. when cast-crucible steel was created.
The term "sand casting" can also refer to an object produced via the sand casting process. Sand castings are produced in specialized factories called foundries. In 2003, over 60% of all metal castings were produced via sand casting. [1] Molds made of sand are relatively cheap, and sufficiently refractory even for steel foundry use.
In the simplest sand casting procedure, the drag is placed upside down on a board, around a pattern of the part to be cast. The pattern is a model of the desired casting. Talcum powder is often dusted over the pattern to aid in the removal of the pattern. Sand is sifted over the pattern until the model is covered by a few inches of sand.
In casting, a pattern is a replica of the object to be cast, used to form the sand mould cavity into which molten metal is poured during the casting process. Once the pattern has been used to form the sand mould cavity, the pattern is then removed, molten metal is then poured into the sand mould cavity to produce the casting.
Another type of binder process is called the hot-box process, which uses a thermoset and catalyst for a binder. The sand with the binder is packed into a core box that is heated to approximately 230 °C (446 °F) (which is where the name originated from). The binder that touches the hot surface of the core box begins to cure within 10 to 30 ...
DISAMATIC consists of a molding machine and mold transporting conveyor. A molding sand mixture, usually green sand or bentonite, is blown into a rectangular steel chamber using compressed air. The molding sand is then squeezed between two patterns, which are on the two ends of the chamber. After squeezing, one of the chamber plates swings open ...
A flask is a type of tooling used to contain a mold in metal casting. A flask has only sides, and no top or bottom, and forms a frame around the mold, which is typically made of molding sand. The shape of a flask may be square, rectangular, round or any convenient shape.
A stationary sand slinger is a type of machine used for filling and uniform ramming of sand in casting molds, and is particularly advantageous with large molds.This machine consists of a heavy base, a bin or hopper to carry sand, and a bucket elevator to which a number of buckets and a swinging arm are attached, which carries a conveyor belt and the sand impeller head.