In materials science, quenching is the rapid cooling of a workpiece in water, gas, oil, polymer, air, or other fluids to obtain certain material properties. A type of heat treating , quenching prevents undesired low-temperature processes, such as phase transformations, from occurring.
Heat treatment techniques include annealing, case hardening, precipitation strengthening, tempering, carburizing, normalizing and quenching. Although the term heat treatment applies only to processes where the heating and cooling are done for the specific purpose of altering properties intentionally, heating and cooling often occur incidentally ...
Martempering is also known as stepped quenching or interrupted quenching. In this process, steel is heated above the upper critical point (above the transformation range) and then quenched in a hot-oil, molten-salt, or molten-lead bath kept at a temperature of 150-300 °C. The workpiece is held at this temperature above martensite start (Ms ...
Molten salts (fluoride, chloride, and nitrate) can be used as heat transfer fluids as well as for thermal storage. This thermal storage is used in concentrated solar power plants. [8] [9] Molten-salt reactors are a type of nuclear reactor that uses molten salt(s) as a coolant or as a solvent in which the fissile material is dissolved ...
In austempering the heat treat load is quenched to a temperature which is typically above the Martensite start of the austenite and held. In some patented processes the parts are quenched just below the Martensite start so that the resulting microstructure is a controlled mixture of Martensite and Bainite.
Once removed from the oven, the workpieces are often quickly cooled off in a process known as quench hardening. Typical methods of quench hardening materials involve media such as air, water, oil, or salt. Salt is used as a medium for quenching usually in the form of brine (salt water). Brine provides faster cooling rates than water.
Differential hardening is a method used in heat treating swords and knives to increase the hardness of the edge without making the whole blade brittle. To achieve this, the edge is cooled faster than the spine by adding a heat insulator to the spine before quenching. Clay or another material is used for insulation. To prevent cracking and loss ...
Induction heating is a non contact heating process which uses the principle of electromagnetic induction to produce heat inside the surface layer of a work-piece. By placing a conductive material into a strong alternating magnetic field, electric current can be made to flow in the material thereby creating heat due to the I 2 R losses in the material.