SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.
Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel). [6] The Japanese equivalent grade of this material is SUS304.
It consists of a prefix letter and five digits designating a material composition. For example, a prefix of S indicates stainless steel alloys, C indicates copper, brass, or bronze alloys, T indicates tool steels, and so on. The first 3 digits often match older 3-digit numbering systems, while the last 2 digits indicate more modern variations.
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. PREN is frequently specified when stainless steels will be exposed to seawater or other high chloride solutions. In some instances stainless steels with PREN-values > 32 may provide useful resistance to pitting corrosion in ...
Type 410 is a general purpose grade containing 0.15% maximum carbon. Type 420 increases the carbon content to 0.15% mininum for improved strength; Type 431 has added nickel content for improved corrosion resistance; Types 440A, 440B and 440C increases the carbon content . Type 440C contains 0.95-1.20% carbon for highest hardness.