The history of molding sand is difficult to study, as much of the origins of the practice predate writing. Molding sand was used exclusively for bronze casts, which was pioneered by the ancient Chinese. The next major advancement came in India in 500 B.C. when cast-crucible steel was created.
The cope and drag (top and bottom halves, respectively) of a sand mold, with cores in place on the drag. Two sets of castings (bronze and aluminium) from the above sand mold. Sand casting, also known as sand molded casting, is a metal casting process characterized by using sand—known as casting sand—as the mold material. The term "sand ...
A molding sand mixture, usually green sand or bentonite, is blown into a rectangular steel chamber using compressed air. The molding sand is then squeezed between two patterns, which are on the two ends of the chamber. After squeezing, one of the chamber plates swings open and the opposite plate pushes the finished mold onto a conveyor.
Sand is sifted over the pattern until the model is covered by a few inches of sand. More sand is then dumped into the drag, and rammed with a wooden wedge, or mechanically vibrated to pack the sand down. The sand is then struck level with the top edge of the drag, using a wooden or metal strake. A board is then placed on top of the drag and the ...
For the production of gray iron, ductile iron and steel castings, sand casting remains the most widely used process. For aluminum castings, sand casting represents about 12% of the total tonnage by weight (surpassed only by die casting at 57%, and semi-permanent and permanent mold at 19%; based on 2006 shipments). The exact process and pattern ...
The direct molding method is to make the wax material into the same wax mold as the casting by hand or other tools; the indirect molding method is to make the wax mold through the mold. The direct molding method requires craftsmen to have a high technical level; otherwise, the quality of castings cannot be guaranteed.
Shell molding is similar to sand casting, but the molding cavity is formed by a hardened "shell" of sand instead of a flask filled with sand. The sand used is finer than sand casting sand and is mixed with a resin so that it can be heated by the pattern and hardened into a shell around the pattern. Because of the resin and finer sand, it gives ...
This allows the entire mold to be made from green sand and from removable patterns. The disadvantage of this is more mold-making operations are required, but it is usually advantageous when the quantities are low. However, if large quantities of casting are required, it is usually more cost effective to simply use a core. [6]