Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture.Rust consists of hydrous iron(III) oxides (Fe 2 O 3 ·nH 2 O) and iron(III) oxide-hydroxide (FeO(OH), Fe(OH) 3), and is typically associated with the corrosion of refined iron.
v. t. e. Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [1][2]
Tempering (metallurgy) Differentially tempered steel. The various colors produced indicate the temperature the steel was heated to. Light straw indicates 204 °C (399 °F) and light blue indicates 337 °C (639 °F). [1][2] Tempering is a process of heat treating, which is used to increase the toughness of iron -based alloys.
Martensite in AISI 4140 steel. 0.35% carbon steel, water-quenched from 870 °C. Martensite is a very hard form of steel crystalline structure. It is named after German metallurgist Adolf Martens. By analogy the term can also refer to any crystal structure that is formed by diffusionless transformation. [ 1 ]
Pitting corrosion. Appearance. Severe pitting corrosion problems caused by chloride ions on a truss beam of the Nandu River Iron Bridge (Hainan Province, China) leading to the complete rupture of a metallic element. Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal.
Thermite (/ ˈθɜːrmaɪt /) [ 1 ] is a pyrotechnic composition of metal powder and metal oxide. When ignited by heat or chemical reaction, thermite undergoes an exothermic reduction-oxidation (redox) reaction. Most varieties are not explosive, but can create brief bursts of heat and high temperature in a small area.
The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components. A definition is "the displacement of building elements due to the expansion of iron and steel products as the metal rusts and ...
This process is easily observed while working a material (by a process of cold working in metals). Theoretically, the strength of a material with no dislocations will be extremely high ( σ ≈ G 10 {\displaystyle \sigma \approx {\frac {G}{10}}} ) because plastic deformation would require the breaking of many bonds simultaneously.