The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The strength of materials is determined using various methods of calculating the stresses and strains in structural members, such as beams, columns, and shafts. The methods employed to predict the response of a structure under loading and its susceptibility to various failure modes takes into account the properties of the materials such as its yield strength, ultimate strength, Young's modulus ...
Commercially pure (99.2% pure) grades of titanium have ultimate tensile strength of about 434 MPa (63,000 psi), equal to that of common, low-grade steel alloys, but are less dense. Titanium is 60% denser than aluminium, but more than twice as strong [ 16 ] as the most commonly used 6061-T6 aluminium alloy .
17-4 stainless steel can be heat treated to approximately 44 Rc, [1] and an ultimate tensile strength of 1,300 MPa (190,000 psi). Its density ranges from 7,800 to 7,900 kg/m 3 (0.282 to 0.284 lb/cu in), and its modulus of elasticity ranges from 197 to 207 GPa (28.5 × 10 ^ 6 to 30.0 × 10 ^ 6 psi).
[3] 0.2% proof and ultimate tensile strength of the Fe–55Mn–3Al–3Si wt% TWIP steel as a function of the test temperature; strain rate ε=10 −4.s −1. [3] Austenitic steels are used widely in many applications because of their excellent strength and ductility combined with good wear and corrosion resistance.
This region starts as the stress goes beyond the yielding point, reaching a maximum at the ultimate strength point, which is the maximal stress that can be sustained and is called the ultimate tensile strength (UTS). In this region, the stress mainly increases as the material elongates, except that for some materials such as steel, there is a ...
The original A242 alloy has a yield strength of 50 kilopounds per square inch (340 MPa) and ultimate tensile strength of 70 ksi (480 MPa) for light-medium rolled shapes and plates up to 0.75 inches (19 mm) thick. It has yield strength of 46 ksi (320 MPa) and ultimate strength of 67 ksi (460 MPa) for medium weight rolled shapes and plates from 0 ...
Both the low nickel content and the high strength (enabling thinner sections to be used) give significant cost benefits. Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ...