Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used. [1]
The main ingredients of an electroless nickel plating bath are source of nickel cations Ni 2+, usually nickel sulfate and a suitable reducing agent, such as hypophosphite H 2 PO − 2 or borohydride BH − 4. [1] With hypophosphite, the main reaction that produces the nickel plating yields orthophosphite H 2 PO − 3, elemental phosphorus ...
Electroless deposition is an important process in the electronic industry for metallization of substrates. Other metallization of substrates also include physical vapor deposition (PVD), chemical vapor deposition (CVD), and electroplating which produce thin metal films but require high temperature, vacuum, and a power source respectively. [20]
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
Nickel plating Soon after, John Wright of Birmingham , England discovered that potassium cyanide was a suitable electrolyte for gold and silver electroplating. Wright's associates, George Elkington and Henry Elkington were awarded the first patents for electroplating in 1840.
Nickel plating may refer to: Nickel electroplating , a technique of electroplating a thin layer of nickel onto a metal object Electroless nickel-phosphorus plating , an auto-catalytic chemical technique used to deposit a layer of nickel-phosphorus on a solid workpiece